Implementation of innovative Si (silicon) fortified cast iron on the market thanks to the development of a dedicated technology of melting and after-burning, eliminating the tendency to create Chunky graphite and porosity of castings and guaranteeing the stability of the performance of cast iron (Q2686854)
Jump to navigation
Jump to search
Project Q2686854 in Poland
| Language | Label | Description | Also known as |
|---|---|---|---|
| English | Implementation of innovative Si (silicon) fortified cast iron on the market thanks to the development of a dedicated technology of melting and after-burning, eliminating the tendency to create Chunky graphite and porosity of castings and guaranteeing the stability of the performance of cast iron |
Project Q2686854 in Poland |
Statements
1,627,966.45 zloty
0 references
2,841,118.08 zloty
0 references
57.3 percent
0 references
1 July 2020
0 references
30 September 2023
0 references
SPÓŁKA AKCYJNA ODLEWNIE POLSKIE
0 references
51°2'18.2"N, 21°4'55.2"E
0 references
Przedmiotem projektu jest opracowanie i przygot. do wdrożenia na rynek żeliwa umocnionego roztworowo krzemem dzięki ulepszonej technologii metalurgiczno-odlewniczej, eliminującej skłonność tego tworzywa do degeneracji grafitu kulkowego, generowania wad skurczowych w odlewach i negatywnie wpływającej na jego właściwości użytkowe.Wyeliminowanie tej bariery technologicznej i wprowadzenie na rynek nowego żeliwa będzie szansą dla producentów komponentów odlewniczych na zaoferowanie klientom możliwości wytworzenia lżejszych i trwalszych części maszyn, urządzeń i pojazdów,odporniejszych zmęczeniowo i trwalszych eksploatacyjnie.Projekt wpisuje się pozytywnym wpływem w zasadę zrównoważonego rozwoju,przez zmniejszony udział surowców pierwotnych(surówka żelaza)w jednostkowym lżejszym wyrobie Założony w projekcie cel zostanie zrealizowany dzięki m.in. pracom B+R w zakresie: •poznania wpływu parametrów procesowych na powstawanie grafitu Chunky w żeliwie sferoidalnym •modyfikacji austenitu rozdrabniającej pierwotne ziarno i zmniejszającej segregację krzemu •efektywnej modyfikacji grafitu do postaci kulkowej •stosowania mikrododatków aktywnych ograniczających degradację grafitu •doboru optymalnego składu żeliwa •testowania w warunkach lab. i na platformie bad. w warunkach operacyjnych kompleks. zabiegów w ciekłym stopie, determinujących krystalizację grafitu kulkowego Numer_referencyjny_programu_pomocowego: SA.41471(2015/X) Przeznaczenie_pomocy_publicznej: art: 25 rozporządzenia KE nr 651/2014 z dnia 17 czerwca 2014 r. uznające niektóre rodzaje pomocy za zgodne z rynkiem wewnętrznym w stosowaniu art. 107 i 108 Traktatu (Dz. Urz. UE L 187/1 z 26.06.2014). (Polish)
0 references
The subject of the project is to develop and prepare for the market of silicon reinforced cast iron thanks to improved metallurgical and casting technology, eliminating the tendency of this material to degeneration of ball graphite, generating shrinkage defects in castings and negatively affecting its performance. Elimination of this technological barrier and the introduction of a new cast iron will be an opportunity for manufacturers of casting components to offer customers the opportunity to produce lighter and more durable parts of machinery, equipment and vehicles, more fatigue-proof and more durable. •recognition of the influence of process parameters on the formation of Chunky graphite in ductile cast iron •modification of austenite shredding primary grain and reducing silicon segregation •effective modification of graphite to ball form •the use of active micro-additions limiting the degradation of graphite •choice of optimal cast iron composition •testing in lab conditions and on the platform bad. under operational conditions complex. treatments in liquid alloy, determining the crystallisation of ball graphite Number_reference_aid_program: SA.41471(2015/X) Purpose_public_aid: Article: 25 of Commission Regulation (EU) No 651/2014 of 17 June 2014 declaring certain categories of aid compatible with the internal market in the application of Articles 107 and 108 of the Treaty Urz. EU L 187/1 of 26.06.2014). (English)
7 July 2021
0 references
L’objectif du projet est de développer et de préparer le marché de la fonte renforcée au silicium grâce à l’amélioration de la technologie métallurgique et de coulée, en éliminant la tendance de ce matériau à la dégénérescence du graphite à bille, générant des défauts de rétrécissement des coulées et affectant négativement ses performances. L’élimination de cette barrière technologique et l’introduction d’une nouvelle fonte seront l’occasion pour les fabricants de composants de coulée d’offrir aux clients la possibilité de produire des pièces plus légères et plus durables de machines, d’équipements et de véhicules, plus résistantes à la fatigue et plus durables. •reconnaissance de l’influence des paramètres de processus sur la formation du graphite Chunky dans la fonte ductile •modification du grain primaire déchiqueté austénite et réduction de la ségrégation du silicium •modification effective du graphite en forme de bille •utilisation de micro-additions actives limitant la dégradation du graphite •choix de la composition optimale en fonte •tests en laboratoire et sur la plate-forme mal. dans des conditions opérationnelles complexes. traitements en alliage liquide, déterminant la cristallisation du graphite à bille Number_reference_aid_program: SA.41471(2015/X) But_public_aid: Article: 25 du règlement (UE) no 651/2014 de la Commission du 17 juin 2014 déclarant certaines catégories d’aides compatibles avec le marché intérieur en application des articles 107 et 108 du traité URZ. EU L 187/1 du 26.6.2014). (French)