Testing of non-ferrous alloy testing for an external overpressure vessel (Q10847): Difference between revisions

From EU Knowledge Graph
Jump to navigation Jump to search
(‎Removed claim: summary (P836): The project deals with the characterisation of the aluminium alloy set A357, after de-joining, after casting the shell. This characterisation will be directly linked to the technological process of temperature management following the casting of the alloy in form until complete cooling before the next technological process. Output shall be a technical report with a recommendation to achieve the maximum strength of alloys. a., remove_old_englis...)
(‎Created claim: summary (P836): The project deals with characterisation of A357 aluminium alloy after controlled cooling after casting into shell form. This characterisation will have a direct link to the technological process of temperature control after casting the alloy into the mould until its complete cooling before the next technological process. The output will be a technical report with a recommendation to achieve the maximum strength of the alloy. a., translated_summary)
Property / summary
 
The project deals with characterisation of A357 aluminium alloy after controlled cooling after casting into shell form. This characterisation will have a direct link to the technological process of temperature control after casting the alloy into the mould until its complete cooling before the next technological process. The output will be a technical report with a recommendation to achieve the maximum strength of the alloy. a. (English)
Property / summary: The project deals with characterisation of A357 aluminium alloy after controlled cooling after casting into shell form. This characterisation will have a direct link to the technological process of temperature control after casting the alloy into the mould until its complete cooling before the next technological process. The output will be a technical report with a recommendation to achieve the maximum strength of the alloy. a. (English) / rank
 
Normal rank
Property / summary: The project deals with characterisation of A357 aluminium alloy after controlled cooling after casting into shell form. This characterisation will have a direct link to the technological process of temperature control after casting the alloy into the mould until its complete cooling before the next technological process. The output will be a technical report with a recommendation to achieve the maximum strength of the alloy. a. (English) / qualifier
 
point in time: 22 October 2020
Timestamp+2020-10-22T00:00:00Z
Timezone+00:00
CalendarGregorian
Precision1 day
Before0
After0

Revision as of 15:13, 22 October 2020

Project in Czech Republic financed by DG Regio
Language Label Description Also known as
English
Testing of non-ferrous alloy testing for an external overpressure vessel
Project in Czech Republic financed by DG Regio

    Statements

    0 references
    0 references
    202,500.0 Czech koruna
    0 references
    8,100.0 Euro
    10 January 2020
    0 references
    270,000.0 Czech koruna
    0 references
    10,800.0 Euro
    10 January 2020
    0 references
    75 percent
    0 references
    13 August 2019
    0 references
    16 April 2018
    0 references
    NANOGIES s.r.o.
    0 references
    0 references

    50°4'5.48"N, 14°27'29.48"E
    0 references
    10100
    0 references
    Projekt se zabývá charakterizací hliníkové slitiny A357 po řízeném ochlazování, po odlití do skořepinové formy. Tato charakterizace bude mít přímou vazbu na technologický postup řízení teploty po odlití předmětné slitiny do formy až do její úplné ochlazení před dalším technologickým postupem. Výstupem bude technická zpráva s doporučením pro dosažení maximální pevnosti slitiny. a. (Czech)
    0 references
    The project deals with characterisation of A357 aluminium alloy after controlled cooling after casting into shell form. This characterisation will have a direct link to the technological process of temperature control after casting the alloy into the mould until its complete cooling before the next technological process. The output will be a technical report with a recommendation to achieve the maximum strength of the alloy. a. (English)
    22 October 2020
    0 references

    Identifiers

    CZ.01.1.02/0.0/0.0/16_045/0010818
    0 references